Preparation and Luminescent Properties of Blue Emitting Phosphor of Sr3(PO4)2∶Eu2+ for White LED
WEI Jian1, SHEN Chang-yu1*, SUN Yu-huan2, ZHANG Hong1, WANG Le1*, LI Chen-xia1
1. Institute of Optoelectronic Technology, China Jiliang University, Hangzhou 310018, China 2. Materials Science and Engineering, Shanghai University, Shanghai 200444, China
Abstract：A series of Sr3(PO4)2∶Eu2+ blue phosphors were synthesized by high temperature solid state method under N2-H2 reducing atmosphere. The crystal structures, excitation and emission spectra were characterized by X-ray diffraction (XRD) and Photoluminescence (PL), respectively. The results show that the Sr3(PO4)2∶Eu2+ phosphor can be efficiently excited by the wavelengths ranging from 310 to 390 nm, and the excitation peak wavelength locates at 359 nm. A wide emission spectrum (～150 nm, originating from the 4f65d1→4f7 of the Eu2+) with a peaking wavelength of 438 nm was obtained. Through the Gaussian fitting, we found that the emission band formed by two luminescence centers（430 and 459 nm）, which indicated that the Eu2+ occupied two different Sr2+ sites in the substrate of Sr3(PO4)2. As the Eu2+ doping concentration is 7%, the maximum luminous intensity was obtained. With the increasing of the doping concentration of the Eu2+, the concentration quenching effect occurred, and the emission peak wavelength has a red shift. The PL intensity of the Sr3(PO4)2∶Eu2+ phosphor is about 1.3 times than that of the blue emitting phosphor BaMgAl10O17∶Eu2+(BAM) which means that it is a promising candidate for the blue phosphor material for white LED.
魏 健1，沈常宇1*，孙玉环2，张 宏1，王 乐1*，李晨霞1 . 白光LED用Sr3(PO4)2∶Eu2+蓝色荧光粉的制备及发光性能研究 [J]. 光谱学与光谱分析, 2015, 35(11): 3028-3031.
WEI Jian1, SHEN Chang-yu1*, SUN Yu-huan2, ZHANG Hong1, WANG Le1*, LI Chen-xia1 . Preparation and Luminescent Properties of Blue Emitting Phosphor of Sr3(PO4)2∶Eu2+ for White LED. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(11): 3028-3031.
[1] Ye S, Xiao F, Pan Y X, et al. Materials Science and Engineering R., 2010, 7: 1. [2] Lin C C, Liu R S. J. Phys. Chem. Lett., 2011, 2: 1268. [3] Guo C F, Luan L, Ding X, et al. Appl. Phys. B, 2009, 95: 779. [4] Xie R J, Hirosaki N, Kimura N, et al. Appl. Phys. Lett., 2007, 90: 191101. [5] Hou B, Rao H, Li J. J. Display Technol., 2009, 5: 57. [6] Wang Z, Liang H, Gong M, et al. J. Alloys and Compounds, 2007, 432: 308. [7] Hirosaki N, Xie R J, Inoue K, et al. Appl. Phys. Lett., 2007, 91: 061101. [8] LIU Dan, LIANG Pei, WANG Le, et al(刘 丹, 梁 培, 王 乐, 等). Acta Phys. Sin.(物理学报), 2013, 62: 197802. [9] Guo N, Huang Y J, You H P, et al. Inorg. Chen., 2010, 49: 10907. [10] Jiang Z Q, Wang Y H. Electrochen, Solid-StateLett., 2010, 13: J68. [11] LIAO Qiu-rong , ZHUANG Wei-dong, XIA Tian, et al(廖秋荣, 庄卫东, 夏 天，等). Acta Phys. Sin.(物理学报), 2009, 4: 2776. [12] Onuma H, Tanno H, Suzuki A, et al. J. Soc. Inf. Display, 2010, 18: 211. [13] Chiu Y C, Liu W R, Chang C K, et al. J. Mater. Chem., 2010, 20: 1755. [14] WANG Zhi-jun, LI Pan-lai(王志军, 李盼来). Acta Phys. Sin.(物理学报), 2014, 63: 77802. [15] CAO Shi-xiu, HAN Tao, TU Ming-jin. Acta Phys. Sin., 2011, 60: 127802.