Preparation and Study on the Spectra of Conductive Nano-Silver Film
MO Li-xin1,LI Lu-hai1*,LI Ya-ling1,HAO Ya-ling1,MENG Tao1,WANG Yan-hui2
1. Lab of Printing & Packaging Material and Technology, Beijing Area Major Lab, Beijing Institute of Graphic Communication, Beijing 102600, China 2. Beijing University of Chemical Technology, The Key Laboratory of Science and Technology of Controllable Chemical Reactions, Ministry of Education, Beijing 100029, China
Abstract：The preparation and study on the spectra of conductive nano-silver film were done under mild conditions. The silver citrate emulsion coating on the surface of PET was reduced by ascorbic acid (Vc) aqueous solution to prepare a silver film. The morphology, crystal structure, surface roughness and conductivity of the silver film were measured by FTIR, UV-Vis spectrum, X-ray diffraction (XRD), scanning electron microscope, scanning probe microscope system and so on. It was found that the silver citrate emumsion has a homogenous particle distribution from 60 nm-150 nm. The UV-Vis spectrum of the silver film shows a peak at 430 nm, and the silver thin film was considered to have a typical nano-scale structure. By the comparison of the XRD patterns of the films treated and untreated with water, it was concluded that the further deoxidization of silver citrate could be accelerated by water. The crystal structure of the silver film was improved and the surface resistance of the silver film was decreased greatly. The effect of ethanol on the decrease in the resistance of the silver film is much less than that of water.
莫黎昕1,李路海1*,李亚玲1,郝雅玲1,孟涛1,王艳辉2 . 纳米银导电膜的制备及其光谱学分析[J]. 光谱学与光谱分析, 2007, 27(12): 2502-2505.
MO Li-xin1,LI Lu-hai1*,LI Ya-ling1,HAO Ya-ling1,MENG Tao1,WANG Yan-hui2 . Preparation and Study on the Spectra of Conductive Nano-Silver Film . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(12): 2502-2505.
[1] WANG Ai-li, YIN Heng-bo, REN Min, et al(王爱丽，殷恒波，任 敏，等). Precions Metals(贵金属)，2006，27(2)：27. [2] Suszynska M, Krajczyk L, Capelletti R. Journal of Non-Crystalline Solids, 2003, 315: 114. [3] Nersisyan H H, Lee J H, Son H T. Materials Research Bulletin, 2003, 38: 949. [4] PAN Wei, ZHANG Xiao-kai, HUANG Ming-hu, et al(潘 伟，张晓凯，黄明湖，等). Electrochemistry(电化学)，2006，12(4)：398. [5] XIONG Xiang-yu(熊祥玉). Screen Printing(丝网印刷)，2005，5：14. [6] Takeo Kawase, Tatsuya Shimoda, Christopher Newsome, et al. Thin Solid Films，2003，438-439: 279. [7] Dongjo Kim, Jooho Moon. Eletrochemical and Solid-State Letters, 2005, 8(11): 530. [8] LAI Xiao-zheng, LAI Sheng-li, ZHANG Rui-na(赖晓铮，赖声礼，张瑞娜). Science Technology and Engineering，2006, 6(14): 1671. [9] Zongtao Zhang, Bin Zhao, Liming Hu. Journal of Solid State Chemistry, 1996, 121: 105-110. [10] ZHOU Quan-fa, XU Zheng, BAO Jian-chun, et al(周全法，徐 正，包建春，等). Fine Chemicals(精细化工)，2001，18(1)：39. [11] ZHANG Ai-ping, FANG Yan(张爱平, 方 炎). Acta Phys.-Chim.(物理化学学报)，2006, 22(6)：756. [12] ZHANG Qing-yu, LI Shi-rong, SI Min-zhen, et al(李清玉, 李世荣, 司民真, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2007, 27(2): 299. [13] ZHANG Ai-guo, WANG Du-jin, XU Yi-zhuang(郑爱国，王笃金，徐怡庄). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2003，23(6)：1132. [14] YUAN Wei-en, JIANG Zhi-liang, PAN Hong-cheng, et al(袁伟恩, 蒋治良, 潘宏程, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2005, 25(6): 920. [15] ZHANG Yun-zhu, DAI Kai, SHI Li-yi, et al(张云竹，代 凯，施利毅，等). New Chemical Materials(化工新型材料)，2006，34(7)：31. [16] MO Li-xin, LI Lu-hai, LI Ya-ling, et al(莫黎昕，李路海，李亚玲，等). Journal of Functional Materials(功能材料)，2000，38：901.