1. 上海应用技术学院化学与环境工程学院,上海 201418 2. 赣南师范学院, 江西 赣州 341000 3. Regenia AB, Stockholm 10691, Sweden
Preparation of Electrodeposited Mo-Ni Coating and Its Spectral Properties
LIU Xiao-zhen1, XIONG Li-ping1, LIU Xiao-zhou2, CHEN Jie3, LUO Yi-fan1, SUN Ying1
1. School of Chemical and Environmental Engineering, Shanghai Institute of Technology, Shanghai 201418, China 2. Gannan Normal University, Ganzhou 341000, China 3. Regenia AB, Stockholm 10691, Sweden
Abstract:Mo-Ni coatings were prepared on Ni alloy by electrodeposition method. The properties of microhardness, wear weight loss and friction coefficients, and thermal expansion of the coatings were investigated, respectively. Mo-Ni coatings were characterized with inductively coupled plasma-atomic emission spectroscopy (ICP-AES), energy-dispersive analyses of X-ray (EDAX), scanning electron microcopy (SEM), and X-ray diffraction (XRD) techniques, respectively. Mo-Ni coating shows higher microhardness, lower wear weight loss and friction coefficient compared with those of Ni alloy. The microhardness of Mo-Ni coating is as high as 518 HV, which is 72.67% higher than that of the Ni alloy (300 HV). The wear weight losses of Mo-Ni coating is 1.94 times lower than that of Ni alloy. The friction coefficient of Ni alloy and Mo-Ni coating are 0.640 and 0.559 respectively. The physical thermal expansion curve of Ni alloy has two the peaks in the ranges of 100~120 and 570~640 ℃ respectively; and that of Ni alloy+Mo-Ni coating has one the peaks in the ranges of 570~640 ℃. The peak of the physical thermal expansion curve of Ni alloy+Mo-Ni coating in the ranges of 570~640 ℃ is much smaller than that of the Ni alloy. Because the part of nickel was replaced by molybdenum in the Ni lattice, molybdenum decreases the lattices transformation of nickel (bcc→fcc). The reason for the formation of the small peak of the physical thermal expansion curve of Ni alloy+Mo-Ni coating in the ranges of 595~625 ℃ is the changes of MoNi4 and MoNi from the semi-crystalline structure to the crystalline structure respectively.
刘小珍1,熊莉萍1,刘小舟2,陈 捷3,罗一凡1,孙 颖1 . 钼镍镀层的制备及其光谱性能 [J]. 光谱学与光谱分析, 2014, 34(04): 1109-1113.
LIU Xiao-zhen1, XIONG Li-ping1, LIU Xiao-zhou2, CHEN Jie3, LUO Yi-fan1, SUN Ying1 . Preparation of Electrodeposited Mo-Ni Coating and Its Spectral Properties . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(04): 1109-1113.
[1] Gupta M, Curry N, Nylén P, et al. Surface and Coatings Technology, 2013, 220: 20. [2] Joulia A, Vardelle M, Rossignol S. Journal of the European Ceramic Society, 2013, 33: 2633. [3] Waki H, Nishikawa I, Kobayashi A. Vacuum, 2013, 88: 93. [4] Keller I, Naumenko D, Quadakkers W J, et al. Surface and Coatings Technology, 2013, 215: 24. [5] Chen H, Hyde T H, Voisey K T, et al. Materials Science and Engineering: A, 2013, 585: 205. [6] Todde S, Licheri R, Orrù R, et al. Chemical Engineering Journal, 2012, 200: 68. [7] Song P, Naumenko D, Vassen R. Surface and Coatings Technology, 2013, 221: 207. [8] Shokati A A, Parvin N, Sabzianpour N, et al. Journal of Alloys and Compounds, 2013, 549: 141. [9] Ho C Y, Patil R B, Wang C C, et al. Surface Science, 2012, 606: 1173. [10] Lamastra F R, Cacciotti I, Bellucci A, et al. Intermetallics, 2012, 22: 241. [11] Liang J J, Wei H, Zhu YL et al. Surface and Coatings Technology, 2012, 206: 2746. [12] Clancy M, Pomeroy M J, Dickinson C. Journal of Alloys and Compounds, 2012, 523: 11. [13] Song M, Guo H B, Abbas M, et al. Surface and Coatings Technology, 2013, 216: 1. [14] Liu X Z, Li X, Yu A B, et al. Journal of Rare Earths, 2009, 27(3): 480. [15] LIU Xiao-zhen, WANG Gang, SONG Ling-ling, et al(刘小珍, 王 刚, 宋玲玲,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2011, 31(7): 1964. [16] LIU Xiao-zhen, CHEN Jie(刘小珍, 陈 捷). China Patent(中国发明专利), CN 201110382777.5, 2011-11-28.