Study on the Occurrence Status of Formamide in Kaolinite-Formamide Intercalation System and the Microstructure of Its Compounds by FTIR and XRD
ZHANG Sheng-hui1, ZHOU Ya-chong1, OU Xue-mei1, QIANG Ying-huai1, XIA Hua2
1. School of Materials Science and Engineering，China University of Mining and Technology，Xuzhou 221008，China 2. Department of Materials Science and Chemistry Engineering，China University of Geoscience，Wuhan 430074，China
Abstract：The objectives of this study are to investigate the possible occurrence status of formamide in the intercalation system, the founction of water and the molecular configurations and orientations of formamide inserted into the interlayer of kaolinite, by washing the products with acetone to eliminate the interferences due to the outersurface absorbed formamide molecules in FTIR spectrometry. The results show that the intercalated, absorbed and free formamide probably exist in the intercalation system. Free formamide is easily to be eliminated selectively by drying, whereas the absorbed formamide is removed only by washing with the proper eluting reagent. H2O also is inserted into the interlayer during the formamide molecules’ intercalation, which is deintercalated after the compounds being dried. Intercalation caused blue shifts of the inner surface OH stretching bands from 3 687 to 3 692 cm-1, and deforming bands from 911 to 906 cm-1 , the bands at 3 651 cm-1 disappeared with a new band appearing at 3 539 cm-1. The frequency of the Si—O bands of kaolinite was slightly shifted. These IR bands changes implied the breaking of the H-bonds between layers of kaolinite, and the formation of new H-bonds between the kaolinite and the inserting formamide molecules in the intercalation compounds. The formamide molecules intercalated were oriented with the C—N bond perpendicular or nearly perpendicular to the (001) surface of the kaolininte and formed 2 types of H-bonding with inner-surface hydroxyls and siloxane layer of the kaolinite respectively through NH2. A novel model was provided to analyse the microstructure of kaolinite-formamide intercalation compounds. The results show that computation data is in good agreement with experimental data.
张生辉1，周亚冲1，欧雪梅1，强颖怀1，夏 华2 . FTIR和XRD研究甲酰胺在高岭石插层复合体系中的形态及其复合物的微观结构 [J]. 光谱学与光谱分析, 2013, 33(11): 2978-2982.
ZHANG Sheng-hui1, ZHOU Ya-chong1, OU Xue-mei1, QIANG Ying-huai1, XIA Hua2 . Study on the Occurrence Status of Formamide in Kaolinite-Formamide Intercalation System and the Microstructure of Its Compounds by FTIR and XRD. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 2978-2982.
[1] Cheng H F，Liu Q F，Cui X N，et al. Journal of Colloid and Interface Science，2012，376：47. [2] Brindley G W，Brown G. Crystal Structures of Clay Minerals and Their X-ray Identification. London：Mineralogical Society，1980. [3] GUO Yong，ZHENG Yu-ying，LONG Hai，et al(郭 勇，郑玉婴，龙 海，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2012，32(1)：99. [4] Deng Y J，Dixon J B，White G N. J. Colloid and Inter. Sci.，2003，257：208. [5] Frost R L，Kristof J，Horvath E. Spectrochimica Acta Part A：Molecular and Biomolecular Spectroscopy，2000，56：1711. [6] Frost R L，Kristof J，Horvath E. Spectrochimica Acta Part A：Molecular and Biomolecular Spectroscopy，2000，56：1191. [7] WANG Lin-jiang，WU Da-qing，YUAN Peng(王林江，吴大清，袁 鹏). Chem. J. Chinese Universities(高等学校化学学报)，2002，23：1948. [8] Gardolinski J E，Ramos L P，Wypych F，et al. Jourmal of Colloid and Interface Science，2000，221：284. [9] ZHANG Sheng-hui，YANG Yang，QIANG Ying-huai(张生辉，杨 杨，强颖怀). Journal of China Ceramic Society(硅酸盐学报)，2006，34：1124. [10] Xie Xiulan，Hayashi S. Journal of Physical Chemistry B，1999，103(29)：5949. [11] Cheng H F，Liu Q F，Frost R L，et al. J. Therm. Anal. Calorim.，2011，103：507. [12] Komori Y，Yoshiyuki S，Kuroda K. Applied Clay Science，1999，15(1-2)：241. [13] Johnston C T，Stone D A. Clays and Clay Minerals，1990，38：121.