Abstract：The microstructure and fracture morphology of carbon coatings were investigated by means of Raman spectrometer and scanning electron microscopy (SEM), which were prepared by chemical vapor deposition (CVD) on the surface of SiC fiber with C2H2+H2 and C2H2+C3H8+Ar as the reactants. The results show that the spectra of the carbon coating contain characteristic D, D” and G peaks around 1 350, 1 400～1 500 and 1 600 cm-1 respectively, indicating a disordered-graphite structure with a small amount of amorphous carbon. The size of microcrystallite increased with the increase in temperature, and the degree of order, together with the uniformity in the carbon coating was improved simultaneously. It was observed on the fracture surface that coatings prepared by C2H2+H2 are flat and dense, whereas those prepared by C2H2+C3H8+Ar exhibit a flexural lamellar structure, which should be attributed to the relatively low degree of order and the non-uniformity in the microstructure.
刘 帅，杨延清*，罗 贤，张荣军，赵光明，金 娜，肖志远 . CVD法SiC纤维表面碳涂层结构的拉曼光谱研究 [J]. 光谱学与光谱分析, 2012, 32(12): 3253-3257.
LIU Shuai, YANG Yan-qing*, LUO Xian, ZHANG Rong-jun, ZHAO Guang-ming, JIN Na, XIAO Zhi-yuan . Investigation of Microstructure of CVD Carbon Coating on SiC Fiber by Raman Spectrometer . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(12): 3253-3257.
[1] YANG Yan-qing，ZHU Yan，CHEN Yan，et al(杨延清，朱 艳，陈 彦，等). Rare Metal Materials and Engineering(稀有金属材料与工程)，2002，31(3)：201. [2] Guo Z X，Derby B. Progress in Materials Science，1995，39：411. [3] Loszewski R C. U.S. Patent，5024889，1991. [4] Oberlin A. Carbon，2002，40：7. [5] ZHANG Rong-jun，YANG Yan-qing，WANG Chen，et al(张荣军，杨延清，王 晨，等). Journal of Inorganic Materials(无机材料学报)，2010，25(12)：1281. [6] Tuinstra F，Koeing J L. Journal of Chemical Physics，1970，53(3)：1126. [7] Vallerot J M，Bourrat X，Mouchon A，et al. Carbon，2006，44：1833. [8] Cheng T T，Jones I P，Shatwell R A，et al. Materials Science and Engineering A，1999，260：139. [9] Zhao Guangming，Yang Yanqing，Zhang Wei，et al. Physica B，2011，406：3876. [10] Yoshida A，Kaburagi Y，Hishiyama Y. Carbon，2005，44：2333. [11] Bokros J C. Carbon，1965，3(1)：17. [12] Cullis C F，Franklin N H. Proceedings of the Royal Society A，1964，280(1380)：139. [13] Crynes B L，Albright L. I & EC Process Design and Development，1969，8(1)：25. [14] Vignoles G L，Langlais F，Descamps C，et al. Surface and Coatings Technology，2004，(188-189)：241. [15] Carrere N，Lardillier F，Vidal-Sétif M H，et al. Materials Science and Technology，2003，19：669.