Effects of γ Irradiation and O2-Annealing on Optical Spectra of Bi Doped Cadmium Tungstate Crystal
LUO Cai-xiang1, XIA Hai-ping1*, YU Can1, ZHANG Yue-pin1, XU Jun2
1. Key Laboratory of Photo-electronic Materials，Ningbo University，Ningbo 315211, China 2. Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China
Abstract：The Bi doped tungstate of cadmium crystals were O2-annealed at various temperature, and the absorption and emission spectra of O2-annealed Bi doped tungstate of cadmium crystals were investigated. The absorption intensity decreased, and the absorption side band was shifted to blue short wavelength as the increase of annealing temperature. The emissions at 528 nm and 1 078 nm were observed under excited by 373 and 980 nm, which they were attributed to the intrinsic emission of CdWO4 crystal and emission of Bi5+ ion, respectively. After the crystals were O2-annealed, the 528 nm emission intensity enhanced while the 1 078 nm intensity reduced. It was attributed to the transformation of Bi5+ to Bi3+ ions in the annealing process. After O2-annealed, the transmission of the crystal was enhanced obviously and the color of the crystal became weak. It is attributed to the decrease of oxygen vacancy (Vo) in crystal after the crystal was heated in O2 atmosphere. The 1 078 nm emission intensity reduced while the 528 nm intensity enhanced after the crystals were γ-irradiated. It may be due to the transormation of Bi5+ to Bi3+ ions through evolution of γ-irradiated.
[1] Zorenko Y, Pashkovsky M, Voloshinovskii A. Journal of Lumincscence, 2006, 116(1-2): 43. [2] Aucedo E S, O Martínez, Ruiz C M. Journal of Crystal Growth, 2006, 291(2): 416. [3] WANG Xue-jun, XIA Hai-ping(王雪俊，夏海平). Acta Phys. Sin. (物理学报), 2006, 55(10): 5263. [4] Khonthon S, Morimoto S, Arai Y. Ceramic Society Jap, 2007, 115(1340): 259. [5] Okhrimchuk A G, Butvina L N, Dianov E M. Optics Letters, 2008, 33(19): 2182. [6] ZHOU Peng, SU Liang-bi, LI Hong-jun(周 朋, 苏良碧, 李红军). Acta Phys. Sin.(物理学报), 2010, 59(4): 2827. [7] YU Jun, ZHOU Peng, ZHAO Heng-yu(喻 军, 周 朋, 赵衡煜). Acta Phys. Sin. (物理学报), 2010, 59(5): 3538. [8] YU Can, XIA Hai-ping, LUO Cai-xiang(虞 灿, 夏海平, 罗彩香). Chinese Journal of Laser(中国激光), 2010, 37(10): 2610. [9] LUO Cai-xiang, XIA Hai-ping, YU Can, et al(罗彩香, 夏海平, 虞 灿，等). Acta Phys. Sin.(物理学报), 2011, 60(7): 077806. [10] LUO Li-ming, TAO De-jie, WANG Ying-jian(罗丽明, 陶德节, 王英俭). Journal of Synthetic Crystals(人工晶体学报), 2004, 33(5): 820. [11] Kalinko A, Kuzmin A, Evarestov R A. Solid State Communications, 2009, 149: 425. [12] LUO Li-ming, WANG Ying-jian(罗丽明，王英俭). Chinese Journal of Quantum Electronics(量子电子学报), 2008, 25(2): 166. [13] Novoselov A, Yoshikawa A, Nikl M. Nuclear Insteuments and Methods in Physics Research A, 2005, 537: 247. [14] Fujimoto Y. J. Am. Ceram. Soc., 2010, 93(2): 581. [15] Kumada N, Takahashi N, Kinomura N. Journal of Solid State Chemistry, 1996, 126(1): 121. [16] Kumada N, Kinomura N, Sleight A W. <i>Solid State Ionics</i>, 1999, 122(1-4): 183. [17] YANG Bing-xin, HOU Bi-hui, LIANG Ren-you(杨炳忻，侯碧辉，梁任又). Journal of China University of Science and Technology(中国科技大学学报), 1996, 26(4)：496. [18] LI Ming-hua, TENG Yu-jie, LIU Cai-xia(李铭华，滕玉洁，刘彩霞). Journal of Synthetic Crystals(人工晶体学报), 1997, 26(2): 125. [19] LI Ming-hua, SUN Shang-wen, TENG Yu-jie(李铭华，孙尚文，滕玉洁). Piezoelectrics & Acoustooptics(压电和声光), 1997, 19(3): 201, 207.