The Relationship between FTIR Spectra of PVA Film and Its Heat Preservation Capability
CUI Hai-long1, 2, XU Wen-guo1, HE Fu-qing2, WANG Zhao-hui3, JIAO Hong-wen2, LU Shi-xiang1
1. Department of Chemistry, School of Science, Beijing Institute of Technology, Beijing 100081, China 2. Beijing Huadunxuehua Plastics Corporation Co. Ltd., Beijing 100160,China 3. Guangdong Huanan Fine Chemical Research Institute,Xinhui 529141, China
Abstract:Polyvinyl alcohol (PVA), polyethylene (PE) and ethylene-vinyl acetate copolymer (EVA) film was prepared. The optic capability, infrared transmittance and heat preservation capability of the films were studied respectively. The result indicated that the haze degree of the PVA film decreased about 15% and 12% than PE film and EVA film; PVA film transmittance of IR was more or less than other films in the 7~14 μm wavelength range so that the temperature of greenhouse could be increased effectively in daylight. It was just 16.2% about 20% less than EVA film, and 50% less than PE film. The PVA film could be used as agricultural film in greenhouse to promote heat preservation performance greatly.
Key words:Light transmittance;Haze;Absorbance of IR;Transmittance of IR;Heat preservation capability
崔海龙1, 2, 徐文国1, 何福庆2, 王朝晖3, 焦红文2, 卢士香1 . 聚乙烯醇薄膜的红外吸收特性与保温性的关联[J]. 光谱学与光谱分析, 2012, 32(01): 96-98.
CUI Hai-long1, 2, XU Wen-guo1, HE Fu-qing2, WANG Zhao-hui3, JIAO Hong-wen2, LU Shi-xiang1 . The Relationship between FTIR Spectra of PVA Film and Its Heat Preservation Capability. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(01): 96-98.