Abstract:The Eu2+ and Dy3+ ion co-doped Sr3Al2O6 phosphor powders with long afterglow were prepared with high temperature solid-state reaction. The phase and the spectra properties of the material were characterized by X-ray diffraction (XRD) and fluorescence spectrophotometer. It was found that the sample is composed of pure Sr3Al2O6 phase. Furthermore, the emission peak of 537 nm under 360 nm excitation and that of 590 nm excited by 468 nm-light were obtained, respectively, and it is more interesting that the emission peaks were at 537 and 590 nm under 394 nm excitation. The effects of different excitation wavelengths on the emission spectrum were explained reasonably by the effect of nephelauxetic effect and crystal field. It revealed that the two types of luminescence with different color were caused by the differences of the center of gravity of the 5d excited state energy level and the split range of 5d energy level.
Key words:Long afterglow luminescence;Sr3Al2O6;Crystal field effect;Nephelauxetic effect
崔彩娥,李 健,黄 平*,梁丽萍,武银兰 . 不同激发波长对Sr3Al2O6∶Eu2+, Dy3+红色长余辉发光材料发射光谱的影响 [J]. 光谱学与光谱分析, 2012, 32(01): 65-68.
CUI Cai-e, LI Jian, HUANG Ping*, LIANG Li-ping, WU Yin-lan. Effect of Different Excitation Monitoring Wavelengths on Emission Spectrum of Red Long Afterglow Phosphor Sr3Al2O6∶Eu2+, Dy3+ . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(01): 65-68.
[1] Smets B, Rutten J, Hoeks G. Journal of the Electrochemical Society, 1989, 136(7): 2119. [2] Palilla F C, Levine A K, Tomkus M R. Journal of the Electrochemical Society, 1968, 115(6): 642. [3] Matsuzawa T, Aoki Y, Takeuchi N, et al. Journal of the Electrochemical Society, 1996, 143(8): 2670. [4] Nag A, Kutty T R N. Journal of Alloys and Compounds, 2003, 354(1): 221. [5] Capron M, Douy A. Journal of the American Ceramic Society, 2002, 85(12): 3036. [6] Xu Yebin, Lu Peixiang, Huang Guohua, et al. Materials Chemistry and Physics, 2006, 95: 62. [7] LIN Yuan-hua, ZHANG Zhong-tai, ZHANG Feng(林元华, 张中太, 张 枫). Journal of Functional Materials(功能材料), 2001, 32(3): 325. [8] Zhang P, Xu M X, Zheng Z T, et al. Materials Science and Engineering B, 2007, 136: 159. [9] CUI Cai-e, WANG Sen, HUANG Ping(崔彩娥, 王 森, 黄 平). Acta Physica Sinica(物理学报), 2009, 58(5): 3565. [10] Katsuzawa T, Sasajima K, Nabae T, et al. Journal of the American Society, 1998, 81(2): 413. [11] Chang C K, Li W, Huang X J, et al. Journal of Luminescence, 2010, 130: 347. [12] Chakoumakos B C, Lager G A, Fernandez-Baca J A. Acta Cryst. C, 1992, 48: 414. [13] ZHANG Ping(张 平). Researches on Synthesis and Photoluminescence of the Flower-Like Strontium Aluminate Long Persistent Phosphor Powders(花形铝酸锶系长余辉发光粉体合成新工艺及发光性能的研究). Tianjin: Tianjin Uinversity Press(天津: 天津大学出版社), 2006. [14] SUN Jia-yue, SHI Chun-shan, LI You-mo(孙家跃, 石春山, 李有谟). Journal of the Chinese Rare Earth Society(中国稀土学报), 1989, 7: 41.