GaN光电阴极激活后的光谱响应分析
王晓晖,常本康* ,张益军,侯瑞丽,熊雅娟
南京理工大学电子工程与光电技术学院,江苏 南京 210094
The Spectral Response Analysis of Activated GaN Photocathode
WANG Xiao-hui, CHANG Ben-kang* , ZHANG Yi-jun, HOU Rui-li, XIONG Ya-juan
Institute of Electronic Engineering and Optoelectronic Technology, Nanjing University of Science and Technology,Nanjing 210094,China
摘要 : 由于GaN光电阴极的突出性能,其在紫外探测方面有着广泛的应用。文章在超高真空激活系统中,对GaN样品进行了Cs/O激活实验,并分析了激活后反射式的量子效率:在240~350 nm的紫外波段内,量子效率约在30%~10%之间,曲线较为平坦,在240 nm处达到30%的最大值,与国外结果对比后发现,本文获得的GaN光电阴极量子效率在短波段尚有不足。研究了GaN(0001)表面的原子排列,利用3D模拟了表面原子排列模型,并推测了Cs在其表面的吸附情况。
关键词 :GaN光电阴极;量子效率;表面原子排列
Abstract :GaN photocathode has a wide applicaion in ultraviolet detection because of the outstanding performance. GaN photocathode was activated in ultrahigh vacuum (UHV) system by Cs/O, and the reflection-mode quantum efficiency (QE) was analyzed. The QE is 30%~10% corresponding to the wavelength 240~350 nm , and the QE curve is flat. The QE reaches the maximum of 30% at 240 nm. Compared with the abroad result, the QE obtained by us is still inadequate at the short wavelength. The atom arrangement of GaN (0001) was studied. The atom arrangement on the surface was simulated by 3D, and in this way the adsorption of Cs on the GaN(0001) was speculated.
Key words :GaN photocathode;Quantum yield;Arrangement of surface atoms
收稿日期: 2010-11-26
修订日期: 2011-03-18
通讯作者:
常本康
E-mail: bkchang@mail.njust.edu.cn
[1] Moram M A, Sadler T C, Haberlen M, et al. Appl. Phys. Lett., 2010, 97: 261907. [2] Masataka Higashiwaki, Srabanti Chowdhury, Brian L Swenson, et al. Appl. Phys. Lett., 2010, 97: 222104. [3] Wantae Lim, Jae-Hyun Jeong, Jae-Hoon Lee, et al. Appl. Phys. Lett., 2010, 97: 242103. [4] QIAO Jian-liang, CHANG Ben-kang, QIAN Yun-sheng, et al(乔建良,常本康,钱芸生, 等). Acta Phys. Sin.(物理学报), 2010, 59: 3577. [5] QIAO Jian-liang, TIAN Si, CHANG Ben-kang, et al(乔建良,田 思,常本康,等). Acta Phys. Sin.(物理学报), 2009, 58: 5847. [6] JIA Lu, XIE Er-qing, PAN Xiao-jun, et al(贾 璐,谢二庆,潘孝军,等). Acta Phys. Sin.(物理学报), 2009, 58: 3377. [7] ZHOU Mei, ZHAO De-gang(周 梅,赵德刚). Acta Phys. Sin.(物理学报), 2008, 57: 4570. [8] Oswald H W, Siegmund, Anton S Tremsin, et al. Proc. SPIE, 2008, 7021: 70211B. [9] Mizuno, Nihashi I T, Nagai T, et al. Proc. SPIE, 2008, 6945: 69451N. [10] Oswald H W, Siegmund. Nucl. Instr. and Meth. A, 2004, 525: 12. [11] Siegmund O, Vallerga J, Mcphate J. Nucl. Instr. and Meth. A, 2006, 567: 89. [12] Machuca F, Liu Z, Sun Y, et al. J. Vac. Sci. Technol. B, 2003, 21(4): 1863. [13] Uchiyama S, Takagi Y, Niigaki M, et al. Appl. Phys. Lett., 2005, 86: 103511-1. [14] XIE Chang-kun, XU Fa-qiang, DENG Rui, et al(谢长坤,徐法强,邓 锐,等). Acta Phys. Sin.(物理学报), 2002, 51(11): 2606. [15] YUAN Jin-she, CHEN Guang-de, QI Ming, et al(苑进社,陈光德,齐 鸣,等). Acta Phys. Sin.(物理学报), 2001, 50(12): 2429. [16] Machuca F, Sun Y, Liu Z, et al. J. Vac. Sci. Technol. B, 2000, 18(6): 3042.
[1]
. LED作为量子效率仪中单色光的可行性研究 [J]. 光谱学与光谱分析, 2019, 39(11): 3340-3345.
[2]
梁振江;刘海霞*;刘凯铭;牛燕雄;尹贻恒 . 基于1.06 μm波长的谐振腔型石墨烯光电探测器的信噪比分析 [J]. 光谱学与光谱分析, 2017, 37(02): 356-360.
[3]
李 兆;赵西成*;陈利君;江元汝;罗 雷 . 不同方法制备Y3 Al5 O12 ∶Ce3+ 黄色荧光粉的对比研究 [J]. 光谱学与光谱分析, 2015, 35(03): 695-699.
[4]
张立祥;冯良桓;王文武*;徐 航;武莉莉;张静全;李 卫;曾广根 . ZnS/CdS复合窗口层对CdTe太阳能电池短波光谱响应的影响 [J]. 光谱学与光谱分析, 2015, 35(02): 320-324.
[5]
梁小蕊;王 刚*;江炎兰;瞿成利;王秀娟;赵 波 . 水杨醛缩对乙酰基苯胺希夫碱的合成及其荧光性质的理论研究 [J]. 光谱学与光谱分析, 2013, 33(12): 3259-3262.
[6]
韦庆敏;;陆建平;刘国聪;*;梁达文 . LaVO4 ∶Dy3+ 纳米棒的溶剂热合成及其光学性能 [J]. 光谱学与光谱分析, 2012, 32(12): 3329-3334.
[7]
石 峰;;;赵 静;程宏昌;;张益军;熊雅娟;常本康* . 透射式蓝延伸GaAs光电阴极的光电发射特性研究 [J]. 光谱学与光谱分析, 2012, 32(02): 297-301.
[8]
潘再法;刘 爽;朱澄静;徐 娟;刘文涵;王丽丽*. 白光LED用单基质荧光粉BaSrMg(PO4 )2 ∶Eu2+ 的制备及发光性能研究 [J]. 光谱学与光谱分析, 2011, 31(11): 2910-2913.
[9]
李 飙;常本康*;徐 源;杜晓晴;杜玉杰;付小倩;王晓晖;张俊举 . 均匀掺杂和梯度掺杂结构GaN光电阴极性能对比研究 [J]. 光谱学与光谱分析, 2011, 31(08): 2036-2039.
[10]
杜晓晴;田 健;周强富. 利用紫外透射光谱研究透射式GaN光电阴极的材料结构及光学特性 [J]. 光谱学与光谱分析, 2011, 31(06): 1606-1610.
[11]
李 敏;尼启良;董宁宁;陈 波* . 极紫外波段微通道板光电子产出理论分析与实验测量 [J]. 光谱学与光谱分析, 2010, 30(08): 2030-2034.
[12]
杨 智;邹继军;牛 军;张益军;常本康* . 高温Cs激活GaAs光电阴极表面机理研究 [J]. 光谱学与光谱分析, 2010, 30(08): 2038-2042.
[13]
牛 军;;乔建良;;常本康*;杨 智;张益军 . 不同变掺杂结构GaAs光电阴极的光谱特性分析 [J]. 光谱学与光谱分析, 2009, 29(11): 3007-3010.
[14]
孟庆裕;陈宝玖*;许武;王晓君;谢宜华;赖华生;狄伟华;任国仲;赵晓霞;杨艳民. 立方相Y2 O3 :Eu纳米晶中C 2 格位Eu3+ 的5 D 0 能级量子效率 [J]. 光谱学与光谱分析, 2006, 26(08): 1377-1381.