The Influence of the Gain on Ignition and Correction in X-Ray Fluorescence Spectrometry
WANG Qian1, YING Xiao-hu2, ZHANG Jian-bo1
1. Ningbo Entry-Exit Inspection and Quarantine Administration, Ningbo 315012, China 2. Bruker AXS GmbH Beijing Representative Office, Beijing 100081, China
Abstract：Research on the gain on ignition question for preparing ore with fusion sample preparation technique was done, and a new correction method was worked out. After fusion sample preparation, sulphide ore would have a lot of sulfate, which would change the sample matrix dramatically, and the matrix effect was corrected with errors. In this paper, a new solution to measuring gain on ignition was put forward, and it was committed step that the sample having gain on ignition was redefined by sample having loss on ignition. Through conversion, the gain on ignition was corrected by subtraction method, and the matrix effect was corrected by theoretical influence coefficients. The analysis results of redefinition samples were converted into the primal samples lastly. The project took copper concentrates as the experimental object, it was found that the gain on ignition of this method was obviously different from the gravimetric method, but through influence evaluation, this error had little effect on test results, and may be reduced by flux. After correction of the gain on ignition, the standard deviation of the elements calibration curves for Cu, Fe and S were less than 0.14%, 0.074% and 0.14% respectively, which were obviousely superior to 0.21%, 0.15% and 0.19%. The results got from this method were in satisfactory agreement with certified values.
王 谦1，应晓浒2，张建波1. X射线荧光光谱分析样品烧增量的影响及校正[J]. 光谱学与光谱分析, 2011, 31(09): 2574-2577.
WANG Qian1, YING Xiao-hu2, ZHANG Jian-bo1. The Influence of the Gain on Ignition and Correction in X-Ray Fluorescence Spectrometry. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(09): 2574-2577.
[1] Tertian R, Ciaisse F. Principles of Quantitative X-Ray Fluorescence Analysis(X射线荧光定量分析原理). Translated by GAO Xin-hua(高新华，译). Beijing: China Iron&Steel Research Institute Group(北京：钢铁研究总院), 1982. 176. [2] YUAN Han-zhang, LIU Yang, QIN Ying(袁汉章，刘 洋，秦 颖). Chinese Journal of Analysis Laboratory(分析试验室), 1992, 11(2): 52. [3] ZHAO Yao, WANG Zai-tian(赵 耀，王再田). Chinese Journal of Analysis Laboratory(分析试验室), 1999, 18(1): 19. [4] DING Shi-bing, QU Xiao-xia, YUE Chun-lei(丁仕兵，曲晓霞，岳春雷). Metallurgical Analysis(冶金分析), 2006, 26(3): 96. [5] Claisse F, Blanchette J S. Physics and Chemistry of Borate Fusion(硼酸盐熔融的物理与化学). Translated by ZHUO Shang-jun(卓尚军，译). Shanghai: East China University of Science and Technology Press(上海：华东理工大学出版社), 2006. 97.