Abstract:Twenty one doped SrAl2O4 long after-glowed phosphors with 4 series were synthesized by self-propagating high-temperature synthesis method (SHS) with urea-nitrate solution which served as media at 600 ℃. They are SrAl2O4∶Eu2+0.012 5, RE3+0.012 5(RE3+=Ce3+, Pr3+, Nd3+, Tb3+, Dy3+), SrAl2O4∶Eu2+0.012 5, M0.012 5(M=Li+, Be2+, Cd2+, Mn2+, Cu2+, Ag+, Zn2+, Pb2+), SrAl2O4∶Eu2+0.012 5, Dy3+0.012 5, M0.012 5(M=Mn2+, Cu2+, Ag+, Zn2+), and SrAl2O4∶Eu2+0.012 5, Dy3+0.012 5,RE3+0.012 5(RE3+=Ce3+, Pr3+, Nd3+, Tb3+), of which luminescence and after-glowing features were tested. The morphology of all these samples presents a state of porosity and laxity. The samples show an intense emission peak at 514 nm and broad peaks of the excitation spectra at 290~360 nm, Tb3+ and Dy3+ had most effects on luminance and after-glowed time respectively. The SrAl2O4∶Eu2+0.012 5, Dy3+0.012 5 had good luminance and proper after-glowed time as well.
栗 源,赵永亮*,刘永刚,魏晓燕,任 越. 自蔓延高温合成掺杂SrAl2O4稀土长余辉发光粉的研究[J]. 光谱学与光谱分析, 2011, 31(06): 1467-1471.
LI Yuan, ZHAO Yong-liang*, LIU Yong-gang,WEI Xiao-yan,REN Yue. Study on Self-Propagating Synthesis of the Doped SrAl2O4 Rare Earth Long Afterglow Phosphors. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(06): 1467-1471.