Abstract：TiO2 sample was prepared by sol-gel method from chloride titanium. The phase transformation of the prepared TiO2 sample was studied by in-situ XRD and normal XRD in different gas. The experimental results showed that the phase transformation temperatures of TiO2 were different under in-situ or normal XRD in different kinds of gas. The transformation of amorphous TiO2 to anatase was controlled by kinetics before 500 ℃. In-situ XRD showed that the growth of anatase was inhibited, but the transformation of anatase to rutile was accelerated under inactive nitrogen in contrast to air. Also better crystal was obtained under hydrogen than in argon. These all showed that external oxygen might accelerate the growth of TiO2, but reduced gas might partly counteract the negative influence of lack of external oxygen. The mechanism of phase transformation of TiO2 was studied by in-situ XRD in order to control the structure in situ.
马利静，郭烈锦* . 采用原位变温X射线衍射技术研究不同气氛下TiO2的相变机理[J]. 光谱学与光谱分析, 2011, 31(04): 1133-1137.
MA Li-jing，GUO Lie-jin* . Study of the Phase Transformation of TiO2 with In-situ XRD in Different Gas . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(04): 1133-1137.
[1] Ma W H, Lu Z, Zhang M S. Appl. Phys., 1998, A66: 621. [2] ZHU Yong-fa, ZHANG Li, WANG Li, et al(朱永法，张 利，王 莉, 等). Acta Chim. Sinica(化学学报), 2000, 58: 467. [3] MA Li-jing, GUO Lie-jin(马利静，郭烈锦). Acta Chim. Sinica(化学学报), 2006, 64: 863. [4] Wu Nae-lih, Lee Min-shuei, Pon Zern-jin，et al. J. Photochem Photobiol A, 2004, 163: 277. [5] Dutta P K, Gallagherand P K, Jen T. Chem. Mater., 1992, 4: 847. [6] Dutta P K, Gallagher P K, Twu J. Chemistry of Matterials, 1993, 5: 1739. [7] Jiang Y J, Zeng L Z, Wang R P, et al. J. Raman Spectrosc., 1996, 27: 31. [8] Rocquefelte X, Goubin F, Montardi Y, et al. Inorg. Chem., 2005, 44(10): 3589. [9] Serwicka E. Colloids Surf., 1985, 13: 287