Synthesis of the Zn2SiO4∶Eu3+ Red Phosphor by Sol-Gel Method
WU Yang, WANG Yong-sheng*, HE Da-wei*, FU Ming, CHEN Zhen-min, LI Yue, MIAO Feng
Key Laboratory of Luminescence and Optical Information, Ministry of Education, Institute of Optoelectronics Technology, Beijing Jiaotong University, Beijing 100044, China
Abstract:Spherical Zn2SiO4∶Eu3+ phosphors were prepared by a Pechini sol-gel process. The microstructure and luminescent properties of the obtained Zn2SiO4∶Eu3+ particles were well characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and photoluminescence (PL) spectra. The results of SEM demonstrated that the Zn2SiO4∶Eu3+ particles with a diameter about 1~3 μm, which have spherical morphology, emitted an intensive red light emission at 613 nm under excitation at 395 nm. Besides, the effects of the Eu3+ concentration, annealing temperature and charge compensators of Li+ ions on the PL emission intensities were investigated in detail. The investigation showed that the PL intensity increased with the annealing temperature increasing. At the same time, the PL intensity firstly increased and then decreased with the Eu3+ and Li+ concentration increasing.
邬 洋,王永生*,何大伟*,富 鸣,陈震旻,李 玥,苗 锋 . 溶胶-凝胶法制备Zn2SiO4∶Eu3+红色荧光粉 [J]. 光谱学与光谱分析, 2011, 31(04): 890-893.
WU Yang, WANG Yong-sheng*, HE Da-wei*, FU Ming, CHEN Zhen-min, LI Yue, MIAO Feng . Synthesis of the Zn2SiO4∶Eu3+ Red Phosphor by Sol-Gel Method . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(04): 890-893.
[1] YANG Zhi-ping, LIU Yu-feng, WANG Li-wei, et al(杨志平,刘玉峰,王利伟,等). Acta Physica Sinica(物理学报), 2007, 56(1): 546. [2] Pang M L, Lin J, Cheng Z Y, et al. Materials Science and Engineering B, 2003, 100: 124. [3] Hyoung Sun Yoo, Won Bin Im, Sung Wook Kim, et al. Journal of Luminescence, 2010, 130: 153. [4] Wang H, Lin C K, Liu X M, et al. Appl. Phys. Lett., 2005, 87: 181907. [5] Li Yanhong, Hong Guangyan. Journal of Solid State Chemistry, 2005, 178: 645. [6] Wang Yan, Qin Weiping, Zhang Jisen, et al. Optics Communications, 2009, 282: 1148. [7] Wang H, Yu M, Lin C K, et al. Journal of Colloid and Interface Science, 2006, 300: 176. [8] ZHANG Guo-you, ZHAO Xiao-xia, MENG Qing-yu, et al(张国有,赵晓霞,孟庆裕,等). Chinese Journal of Luminescence(发光学报), 2007, 28(1): 57. [9] WENG Zhi-wang, GUO Fan, XIE Jin, et al(翁之望, 郭 范, 谢 瑾, 等). Journal of the Chinese Rare Earth Society(中国稀土学报), 2002, 20(6): 590. [10] Ouyang X, Kitai A H, Xiao T. J. Appl. Phys., 1996, 79: 3229. [11] Justel T, Nikol H, Ronda C. Angew. Chem. Int. Ed., 1998, 37: 3074. [12] Hsieh Hanyu, Lin Sungen, Wei Wencheng. Journal of Luminescence, 2009, 129: 595. [13] Zhang Q Y, Pita K, Kam C H. J. Phys. Chem. Solids, 2003, 649: 333. [14] Patra A, Gray A Baker, Sheila N Baker. Optical Materials, 2004, 27: 15. [15] Selomulya R, Ski S, Pita K, et al. Materials Science and Engineering, 2003, B100: 136. [16] Li C X, Quan Z W, Yang J, et al. Inorg. Chem., 2007, 46: 6329. [17] Meyssamy H, Riwotzki K, Kornowski A, et al. Adv. Mater., 1999, 11: 840. [18] Wei Zhenggui, Sun Lingdong, Liao Chunsheng, et al. Appl. Phys. Lett., 2002, 80(8): 1447. [19] Morell A, Elkhiati N. J. Electrochem. Soc., 1993, 140: 2019.