Study on Preparation and Optical Spectroscopy of Nickle Phthalocyanine-Doped Sol-Gel Materials
ZHAN Hong-bing1，2, CHEN Wen-zhe1, LI Guang-hui1, WANG Min-quan2
1. College of Materials Science and Engineering, Fuzhou University, Fuzhou 350002，China 2. Department of Materials Science and Engineering, Zhejiang University, Hangzhou 310027，China
Abstract：We report here the preparation of nickle tetrasulfo-phthalocyanine (NiTSPc)-doped silica xerogel matrix obtained by sol-gel technique. The evolution of silica matrix′s texture and the rate during the sol-gel process, as well as silica xerogel′s pore structure were studied. Dimerization behavior of NiTSPc molecules was characterized by electronic absorption spectra，and changes in the absorption spectra were correlated with various stages of the sol-gel process. The results show that in the composites NiTSPc concurs in the forms of monomer and dimer，and dimerization is stronger during the latter stages. The reason is given from the change in the micro-environment in which NiTSPc existed during the sol-gel process.
[1] Leznoff C C, Lever A B P. Phthalocyanine Properties and Applications. NewYork: VCH Publishers, Inc.，1989. 397. [2] Shirk J S, Lindle J R. J. Nonlin. Opt. Phys., 1989，1： 699. [3] Sastre A, Diaz-Garcia M A. J. Phys. Chem., 1997，101： 977. [4] QIAN Guo-dong(钱国栋). Study on Preparation Optical Sectroscopy of Inorganic-based Hybrid Nanocomposite Materials for Luminescence Application(无机基有机纳米复合发光材料制备与光谱学基础研究)： [Ph.D.degree thesis(学位论文)].Hangzhou(杭州)： Zhejiang University(浙江大学), 1996. [5] Fuqua P D, Dunn B, Zink Ji. J. Sol-Gel Sci. and Tech., 1998, 11: 241. [6] Haiping Xia, Masayaki Nogami. J. Materials Science, 1999，34： 3053. [7] YAN Ji-min, ZHANG Qi-yuan(严继民，张启元). Absorption and Condensation: The Surface and Pores of Solid(吸附与凝聚： 固体的表面和孔). Beijing: Science Press(北京： 科学出版社), 1979. 67. [8] HUANG Jin-ling, PENG Yi-ru, CHEN Nai-sheng(黄金陵，彭亦如，陈耐生). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2001，21(1)： 1.