Abstract：Tb-doped luminescent SiO2 xerogel was prepared by the sol-gel technique. FTIR was used to measure the microstructure of the luminescent materials. The luminescence properties were characterized by F-7000 UV-visible fluorescence spectrophotometer. The effects of the molar ratio of H2O on the fluorescence and phosphorescence intensity and phosphorescence lifetime of the sample were mainly investigated. The results showed that for the Tb3+ doped xerogels, the sample of 1∶4∶4 annealed at 650 ℃ reaches the maximum intensity, the sample of 1∶4∶5 annealed at 750 ℃ reaches the maximum, the sample of 1∶4∶6 annealed at 850 ℃ is the strongest. With increasing the amount of water, the luminous intensity of the samples annealed at 750 ℃ was first weakened, then enhanced and finally weakened. It was shown that the luminous intensity of samples is related to the molar ratio of aqueous solutions and annealing temperature, whose influence on the luminous intensity formed a competitive mechanism. Phosphorescence was observed at the same time，illustrating the existence of defects in the matrix space, and that the influence of water on the intensity is the same as that of fluorescence. In addition, with the increase in the molar ratio of aqueous solutions, the amount of defect gradually changed and resulted in a change in the luminescence decay time.
潘 静1，胡晓云1*，刘国敬1，张德恺1，樊 君2 . 含水量对Tb∶SiO2光谱特性的影响 [J]. 光谱学与光谱分析, 2010, 30(05): 1179-1183.
PAN Jing1, HU Xiao-yun1*, LIU Guo-jing1, ZHANG De-kai1, FAN Jun2 . Influence of the Amount of H2O on the Emission Spectra of Tb Doped SiO2 Xerogels . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(05): 1179-1183.
[1] Sohn S H, Lee J H, Lee S M. Journal of Luminescence，2009, 129: 478. [2] ZHANG Rui-jun, YAN Wei-ping, MA Ling-zhi(张睿君, 闫卫平, 马灵芝). Chinese Journal of Luminescence(发光学报)，2007, 28(1): 126. [3] LI Jian-yu(李建宇). Rare Earth Luminous Material and Its Application(稀土发光材料及其应用). Beijing: Chemical Industry Press(北京：化学工业出版社)，2003. 127. [4] SONG Chun-feng, YANG Ping, Lü Meng-kai, et al(宋春风, 杨 萍, 吕孟凯, 等). Bulletin of the Chinese Ceramic Society(硅酸盐通报)，2003, 22: 89. [5] HU Xiao-yun, FAN Jun, BAI Jin-tao, et al(胡晓云, 樊 君, 白晋涛, 等). Journal of the Chinese Rare Earth Societ(中国稀土学报)，2005,23(6): 695. [6] ZHANG Zhong-yi, ZHANG Yun-hong, LI Xiao-li, et al(张忠义, 张韫宏, 李晓丽, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2008, 28(8): 1737. [7] HU Xiao-yun, FAN Jun, LI Ting, et al(胡晓云, 樊 君, 李 婷, 等). Acta Photonica Sinica(光子学报), 2005, 34(9): 1340. [8] WU Hong-ying, WENG Shi-fu(吴红英, 翁诗甫). Acta Physico-Chimica Sinica(物理化学学报)，2001, 17(1): 53. [9] LIU Jin-xia(刘金霞). Journal of Synthetic Crystals(人工晶体学报)，2008, 37(2): 342. [10] Zawadzki M, Hreniak D, Wrzyszcz J, et al. Chemical Physics, 2003，291: 275. [11] Han B H, Manners I, Mitchell A W. Chemical Material，2005, 17(12)：3160. [12] ZHANG Zhong-tai(张中太). Non-Organic Luminous Materials and Their Applications(无机光致发光材料及应用). Beijing: Chemical Industry Press(北京：化学工业出版社)，2005. 118. [13] XU Xu-rong, SU Mian-zeng(徐叙瑢, 苏勉曾). Luminescence and Luminescent Materials(发光学与发光材料). Beijing: Chemical Industry Press(北京：化学工业出版社)，2004. 109. [14] HU Xiang，LI Dong-sheng，CHENG Pei-hong, et al(胡 翔, 李东升, 程培红, 等). Chinese Journal of Luminescence(发光学报)，2008, 29(4): 684. [15] ZHENG Zi-qiao, LI Hong-ying(郑子桥, 李红英). Rare Earth Functional Materials(稀土功能材料). Beijing: Chemical Industry Press(北京：化学工业出版社)，2003. 170.