Investigation on Spectroscopic Properties of Yb3+-Doped Laser Glasses
LI Wei-nan, DING Guang-lei, LU Min, XIANG Li-bin
State Key Laboratory of Transient Optics and Photonics，Xi’an Institute of Optics and Precision Mechanics，Chinese Academy of Sciences，Xi’an 710068, China
Abstract：Yb3+-doped borosilicate glasses were prepared at high tempreture. The absorption spectra and fluorescence spectra were measured at room temperature. The integrated absorption cross section, stimulated emission cross section and fluorescent time were calculated. The results showed that the main peak wavelength was 975.15 nm in absorption spectra with one subpeak near 937.17 nm; emission peak was at 977.15 nm in fluorescence spectra with one subpeak near 997.42 nm; with increasing the sample thickness from 0.5 to 5 mm, luminescence intensity became greater, and the peak shifted to longer wavelength from 995.79 to 999.02 nm. The effective line width of fluorescence increased from 34.64 to 54.50 nm; Fluorescence lifetime decreased from 1.04 to 1.00 ms.
[1] DAI Shi-xun, YANG Jian-hu, DAI Neng-li, et al(戴世勋, 杨建虎, 戴能利, 等). Acta Physica Sinica(物理学报)，2003，52(6): 1533. [2] WEN Shang-sheng，FENG Zhou-ming，LIU Yue-hui，et al(文尚胜, 冯洲明, 刘粤惠, 等). Chinese Journal of Quantum Electronics(量子电子学报)，2004，21(4): 419. [3] Weber W J, Lynch J E, Blachburn D H, et al. IEEE J.Quant Electron., 1983，QE-19(10)：1600. [4] Ye D C, Sibley W A. J. Non-Cryst. Solids, 1986, 88(1): 66. [5] Zou Xuelu, Hisayoshi Toratani. Physical Review B, 1995, 52(22): 15889. [6] Takebe H, Murata T, Morinaga K. J. Am. Ceram. Soc., 1996, 79(3)：681. [7] JIANG Chun, ZENG Qing-ji, LIU Hua, et al(姜 淳, 曾庆济, 刘 华, 等). Science in China, Series E(中国科学, E集), 1999, 29(6): 512. [8] MAO Yan-li, DENG Pei-zhen, GAN Fu-xi, et al(毛艳丽, 邓佩珍, 干福熹, 等). Chin. J. Lumin.(发光学报), 2002, 23(2)：152. [9] LI Wei-nan, ZOU Kuai-sheng, LU Min, et al(李玮楠，邹快盛，陆 敏，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2006，26(6)：983. [10] ZHANG Long, LIN Feng-ying, HU He-fang(张 龙, 林凤英, 胡和方). Acta Physica Sinica(物理学报)，2001，50(7): 1378.