Abstract:Core-shell structured ZnS∶Cu/ZnS nano-particles and Cu2+-doped ZnS nano-particles without any shell were prepared, and the effect of ZnS shell on the luminescence properties of ZnS∶Cu2+ nano-particles was studied. The observed emission peak at 450 nm was assigned to the recombination of an electron from the shallow delocalized donor levels at the t2 level of Cu2+. The ZnS shell did enhance the luminescence at 450 nm, which resulted from the reduction of nonradiative recombination sites.
曹立新,孙大可,林映霞. 核-壳结构的ZnS∶Cu/ZnS纳米粒子的制备及发光性质研究[J]. 光谱学与光谱分析, 2006, 26(11): 2000-2002.
CAO Li-xin, SUN Da-ke, LIN Ying-xia. Preparation and Luminescence Properties of Core-Shell ZnS∶Cu/ZnS Nano-Particles . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(11): 2000-2002.
[1] Spanhel L, Haase M, Weller H,et al. J. Am. Chem. Soc., 1987, 109: 5649. [2] Danek M, Jensen K F, Murray C B,et al. Chem. Mater., 1996, 8: 173. [3] Hines M A, Guyot-Sionnest P. J. Phys. Chem., 1996, 100: 468. [4] Harrison M T, Kershaw S V, Rogach A L,et al. Adv. Mater., 2000, 12: 123. [5] Gerion D, Pinaud F, Williams S C, et al. J. Phys. Chem. B, 2001, 105: 8861. [6] TENG Feng, TANG Ai-wei, GAO Yin-hao, et al(滕 枫,唐爱伟,高银浩, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2005,25(5):651. [7] Heesun Y, Paul H H. Appl. Phys. Lett., 2003, 82(12): 1965. [8] Steigerwald M L, Alivisatos A P, Gibson J M, et al. J. Am. Chem. Soc., 1988, 110: 3046. [9] YAO Lian-zeng et al(姚连增, 等). The Basic of Crystal Growth(晶体生长基础). Hefei: Press of University of Science and Technology of China(合肥: 中国科学技术大学出版社),1995. 258. [10] Brus L E. J. Chem. Phys., 1984, 80: 4403. [11] Liu C X, Liu J X, Xu W. Materials Science and Engineering, 2000,B75: 78. [12] Xu S J, Chua S J, Liu B,et al. Appl. Phys. Lett., 1998, 73(4): 478. [13] Wang M, Sun L, Fu X, et al. Solid State Commun., 2000, 115: 493. [14] Yang P, Lu M, Xu D, et al. Chem. Phys. Lett., 2001, 336: 76. [15] Ageeth A B, Joke F, Jaap A B, et al. J. Luminescense, 2002, 99(4): 325. [16] Sang W, Qian Y, Min J, et al. Solid State Commun., 2002, 121(9-10): 475.