Abstract:The concentration of the component of PEG/PE blends was analyzed quantitatively by infrared spectroscopy. The absorption peak area ratio of the selected mixture peaks used as the calibrating basis for the quantitative analysis was more reasonable than the peak area ratio of the pure peaks. The theoretical equation deducted by Beer-Lamber law was used to establish the working curve to calculate the composition of the responding functional groups in the film of the PEG/PE blends. The characteristic peaks of the crystal can not be selected as the calibrating basis for the quantitative measurement, because the crystallization has a great effect on the intensity of the absorption peaks.
[1] Wu Soubeng. Polymer Interface and Adhesion. New York: Marcell Dekker Press, 1982. [2] XUE Qi(薛 奇). The Application of Spectrum in the Study of Polymer Structure(高分子结构研究中的光谱方法). Beijing: High Education Press(北京: 高等教育出版社), 1995. 80. [3] Cole K C, Thomas Y, Pellerin E, et al. Appl. Spectroscopy, 1996, 50(6): 774. [4] Lepatofu U S(利帕托夫 U S). The Handbook of Physical and Chemical Properties of Polymers(聚合物物理化学手册). Semenowech Γ M, Xpamoba T C(谢缅诺维奇 Γ M, 赫拉莫娃 T C). The FTIR and NMR Spectrum of Polymers(聚合物的红外光谱和核磁共振谱). Translated by YAN Jia-bin(闫家宾译). Beijing: China Petrochemical Press(北京: 中国石化出版社), 1995. [5] Jiaxing Chen, Joseph A. Gardella, Jr., Appl. Spectroscopy 1998, 52(3): 361. [6] QIAN Hao, ZHU Ya-fei, XU Jia-rui(钱 浩, 祝亚非, 许家瑞). Spectroscopy and Spectral Anaylsis(光谱学与光谱分析), 2003, 23(4): 708. [7] Giuseppe Zerbi, Germana Gallino. Polymer, 1989, 30: 2324