稀土掺杂长余辉发光玻璃的研究
张希艳,米晓云,肖志义, 刘全生
长春理工大学材料与化工学院,吉林 长春 130022
Study on Rare Earth Doped Long Luminescence Glass
ZHANG Xi-yan,MI Xiao-yun,XIAO Zhi-yi,LIU Quan-sheng
Changchun University of Science and Technology, Changchun 130022,China
摘要 : 分别采用空气气氛和还原气氛,制备了稀土Eu2 O3 ,Dy2 O3 掺杂的铝硅酸盐玻璃,利用荧光光谱仪对样品进行了测试。结果表明:空气气氛条件下制备的铝硅酸盐玻璃样品均不具备长余辉发光性能, 其激发光谱和发光光谱均是Eu3+ 的5 Di (i =0, 1)→7 Fj (j =0~4)跃迁的典型光谱。经还原气氛处理后,单掺和双掺的铝硅酸盐玻璃样品均具有长余辉发光现象,单掺Eu2+ 的发光峰位于462 nm,而双掺Eu2+ 和Dy3+ 的发光峰位于457 nm,且双掺Eu2+ 和Dy3+ 的样品陷阱能级较深,样品的发光持续时间长达12 h以上。
关键词 :长余辉发光;铝硅酸盐玻璃;Eu2 O3 ;Dy2 O3
Abstract :A luminosilicate glass samples doped with Eu2 O3 and Dy2 O3 were prepared under the air and reducing atmosphere respectively. The excitation spectra, emission spectra and thermal luminescence spectra of the samples prepared under different atmosphere were measured. Luminescence mechanism of the afterglow glasses was analyzed. The results showed that the sample prepared under an ambient atmosphere has no afterglow. Its excitation and emission spectra showed the typical transitions of 5 Di (i =0, 1)→7 Fj (j =0-4) from Eu3+ but the sample reheated at a reducing atmosphere has afterglow. The sample doped with Eu2+ shows luminescence peaking at 462 nm. And the sample codoped with Eu2+ and Dy3+ shows luminescence peaking at 457 nm. The afterglow luminescence can last more than 12 h.
Key words :Long afterglow luminescence;Aluminosilicate glass;Eu2 O3 ;Dy2 O3
收稿日期: 2004-06-02
修订日期: 2004-10-18
通讯作者:
张希艳
引用本文:
张希艳,米晓云,肖志义, 刘全生. 稀土掺杂长余辉发光玻璃的研究[J]. 光谱学与光谱分析, 2005, 25(11): 1756-1759.
ZHANG Xi-yan,MI Xiao-yun,XIAO Zhi-yi,LIU Quan-sheng. Study on Rare Earth Doped Long Luminescence Glass. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(11): 1756-1759.
链接本文:
https://www.gpxygpfx.com/CN/Y2005/V25/I11/1756
[1] Qiu J, Shimizugawa Y, Iwabuchi Y, et al. Appl. Phys. Lett., 1997, 71: 759. [2] Qiu J, Shimizugawa Y, Sugimoto N, et al. J. Non-Cryst. Solids, 1997, 213/214: 266. [3] WANG Xiao-jun, LIN Hai, HUANG Li-hui, et al(王晓君, 林 海, 黄立辉, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 1999, 19(5):645. [4] Qiu Jianrong, Miura Kiyotaka, Mitsuyu Tsuneo, et al. SPIE, 1999, 3622: 2. [5] GAN Fu-xi(干福熹). Journal of the Chinese Ceramic Society(硅酸盐学报),1999,27(3):330. [6] ZHANG Jun-ying, ZHANG Lin, WANG Tian-ming(张俊英,张 林,王天明,等). Mater Rev(材料导报), 2003, 17(4): 17. [7] GAN Fu-xi(干福熹). Optical Glass (光学玻璃). Beijing:Science Press( (北京: 科学出版社). 1964. 30. [8] XU Guang-xian(徐光宪). Rare Earth(稀土). Beijing: Metallurgical Industry Press(北京:冶金工业出版社), 1995. 124.
[1]
. Tb3+ 掺杂锂铝硅酸盐玻璃的光致发光和辐照致发光 [J]. 光谱学与光谱分析, 2021, 41(06): 1863-1868.
[2]
. 近红外长余辉材料CaGdAlO4 ∶Cr3+ 的制备及其光学特性 [J]. 光谱学与光谱分析, 2020, 40(02): 373-378.
[3]
. 应力发光材料Sr2 SiO4 ∶Eu, Dy的光谱性质研究 [J]. 光谱学与光谱分析, 2018, 38(07): 2032-2037.
[4]
崔彩娥;李 健;黄 平*;梁丽萍;武银兰 . 不同激发波长对Sr3 Al2 O6 ∶Eu2+ , Dy3+ 红色长余辉发光材料发射光谱的影响 [J]. 光谱学与光谱分析, 2012, 32(01): 65-68.
[5]
刘艳红;;李 斌*;丛 妍; . 静电纺丝纳米ZrO2 ∶Ti纤维的制备与发光性质的研究 [J]. 光谱学与光谱分析, 2010, 30(04): 887-891.
[6]
贺春晖;郑淑华;肖 勇;刘应亮* . 纳米棒状长余辉材料BaAl2 O4 ∶Eu 2+, Dy3+ 的制备与发光性能 [J]. 光谱学与光谱分析, 2010, 30(01): 26-29.
[7]
陈月娥;侯蓝田 . 掺Eu3+ 镉铝硅酸盐玻璃的制备及光谱性质研究 [J]. 光谱学与光谱分析, 2009, 29(05): 1205-1208.
[8]
王光辉;梁小平*;顾玉芬. 硼酸掺量对SrAl2 O4 长余辉发光材料的发光性能影响 [J]. 光谱学与光谱分析, 2008, 28(05): 1020-1022.
[9]
张希艳;姜薇薇;刘 学;卢利平;王晓春;柏朝晖;刘全生;曹志峰 . CaAl2 O4 :Eu2+ , Nd3+ 纳米粉体的合成与发光性质 [J]. 光谱学与光谱分析, 2005, 25(10): 1560-1563.