1. College of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China 2. Department of Chemical and Environment Protection, Changsha Aeronautical Vocation and Technical College, Changsha 410124, China
Abstract：Rare earth organic complexes combined with inorganic compounds can enhanced thermal stability, but inorganic compounds matrix has great influence on the luminescence characteristic of rare earth organic complexes. The luminescence characteristic of organic and inorganic compound material was improved by PEG doping in the material. Eu(BA)3/SiO2 and Eu(BA)3/PEG400-SiO2 were synthesized by Sol-Gel method. The result of luminescence analysis showed that the excitation spectra and emission spectra of Eu(BA)3 accorded with those of Eu(BA)3/SiO2 and Eu(BA)3/PEG400-SiO2, but the luminescence intensity of Eu(BA)3/SiO2 was improved by PEG 400-SiO2 in SiO2 gel. This was because PEG400 as a hard Lewis base, could be combined with rare earth ion and increase the luminescence intensity of Eu(BA)3. It was shown that the amount of PEG400 in Eu(BA)3/SiO2 had influence on luminescence intensity of Eu(BA)3, namely there was better luminescence intensity in Eu(BA)3/SiO2 with increment of the PEG400 addition, but when the amount of PEG400 exceeded 50 wt% of that of SiO2, the luminescnece intensity of Eu(BA)3 hardly increased. When the amount of PEG400 exceed 15 wt% of that of SiO2, PEG400 had little influence on the content of water and hydroxy in the matxix, as verified by IR spectrum. The surface characteristic of SiO2 gel was investigated by atomic force microscopy(AFM).
[1] ZHANG Yong，WANG Min-quan(张 勇，王民权). Journal of Functional Materials(功能材料), 1998, 29(4): 420. [2] Fan Xianping, Wang Feng. Materials Chemistry and Physics, 2003, 82(1): 38. [3] Franville A C, Zambon D. Journal of Alloys and Compounds, 1998, 275-277: 831. [4] Qian Guodong, Wang Minquan. Materials Research Bulletin, 2001, 36: 2289. [5] WANG Xi-gui, WU Hong-ying, XIE Da-tao, et al(王喜贵，吴红英，谢大弢，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2002，22(2): 270. [6] Furlani M, Ferry A. Solid State Ionics, 1998, 113-115: 129. [7] Bekiari V, Pistolis G. Journal of Non-Crystalline Solids, 1998, 226: 200. [8] LIAN Xi-shan, SHENG Hui, LIU Zhan-mei(连锡山，盛 慧, 刘占梅). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 1999, 19(4): 562. [9] ZHANG Yong, WANG Min-quan(张 勇，王民权). Bulletin of the Chinese Ceramics Society(硅酸盐通报), 1999, 18(1): 58. [10] WANG Xi-gui, WU Hong-ying, ZHAO Si-qin, et al(王喜贵，吴红英，赵斯琴，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2006，26(5)：805.