Preparation and Characterization of Magnetic Photocatalysts TiO2 / Fe3 O4
SUN Xiu-yun,WANG Lian-jun* ,WANG Jian,LI Jian-sheng,LI Xin,WANG Jun-de
Department of Environmental Engineering, Nanjing University of Science and Technology, Nanjing 210094, China
摘要 : 以Fe3 O4 为磁核,制备了易于分离的磁性光催化剂。采用X射线粉末衍射(XRD)、扫描电镜(SEM)、光电子能谱(XPS)、傅里叶红外光谱(FTIR)等手段表征催化剂的表面形貌、晶型组成、化学结构等。结果表明,TiO2 包覆在Fe3 O4 表面,且包覆较为牢固。利用降解斯蒂酚酸考察其光催化性能,制得的催化剂具有较高的光催化活性和较好的可分离性。
关键词 :光催化;包覆;TiO2 ;斯蒂酚酸
Abstract :Magnetic photocatalysts (TiO2 / Fe3 O4 ), which are liable to be separated and recovered, were prepared using Fe3 O4 as the support. The surface morphology and crystal pattern were investigated by means of XRD, SEM, XPS and FTIR. The results showed that TiO2 wraps on the surface of Fe3 O4 . The photocatalytic activity of the catalysts was investigated by photocatalytic decolorization of (TNR). The photocatalytic activity of the catalysts is high and the separating ratio is good.
Key words :Photocatalysis;Wrap;Titanium dioxide;2;4;6-Trintroresorcinol
收稿日期: 2006-01-06
修订日期: 2006-04-03
通讯作者:
王连军
引用本文:
孙秀云,王连军* ,王见,李健生,李欣,王俊德 . 磁性光催化剂TiO2 /Fe3 O4 的制备和表征[J]. 光谱学与光谱分析, 2007, 27(04): 777-780.
SUN Xiu-yun,WANG Lian-jun* ,WANG Jian,LI Jian-sheng,LI Xin,WANG Jun-de. Preparation and Characterization of Magnetic Photocatalysts TiO2 / Fe3 O4 . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(04): 777-780.
链接本文:
https://www.gpxygpfx.com/CN/Y2007/V27/I04/777
[1] Hana Krsová, Jarom’r Jirkovsk, et al. Appl. Catal., 2003, 40B: 1. [2] Hiromi Yamashita, Masaru Harada. et al. J. Photochem. Photobio., 2002, 148A: 257. [3] Raffaele Molinari,Michelangelo Borgese, et al. Catal. Today, 2002, 75: 77. [4] J Araáa, O González D’az. Appl. Catal., 2002, 36 B: 113. [5] Prashant V Kamatl, Dan Meisel. Current Opin. Colloid Interface Science, 2002, 7: 282. [6] GUAN Kai-shu, YIN Yan-sheng, JIANG Qiu-peng(关凯书, 尹衍升, 姜秋鹏). Journal of the Chinese Ceramic Society(硅酸盐学报), 2003, 31(3): 219. [7] SU Wen-yue, FU Xian-zhi, WEI Ke-mei, et al(苏文悦, 傅贤智, 魏可镁, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2001, 21(1): 32. [8] YU Xi-bin, WANG Gui-hua, LUO Yan-qing, et al(余锡宾,王桂华, 罗衍庆,等). Acta Chimica Sinca(化学学报), 2000, 58(6): 548. [9] YE Chun-nuan, TANG Nai-yun, WU Xue-mei, et al(叶春暖, 汤乃云, 吴雪梅, 等). Microfabrication Technology(微细加工技术), 2002, (1): 36. [10] YUAN Huan-xin, OUYANG Jian-ming(袁欢欣,欧阳健明). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2007,27(2):395.
[1]
陆燕华,徐敏敏,姚建林. TiO2 -Ag纳米复合材料的制备及其光电催化性能研究 [J]. 光谱学与光谱分析, 2023, 43(04): 1112-1116.
[2]
宗志芳,徐维成,陈德鹏,唐 刚,周晓慧,董 伟,吴玉喜. 基于光谱学分析癸酸-棕榈酸/SiO2 @TiO2 光催化相变微胶囊的制备机理 [J]. 光谱学与光谱分析, 2023, 43(04): 1306-1313.
[3]
齐东丽,程 佳,孙 辉,张芮馨,宋建宇,秦艳利,李宏达,沈龙海. 球磨处理的TiO2 光谱特征及其光催化性能研究 [J]. 光谱学与光谱分析, 2022, 42(10): 3063-3067.
[4]
张利胜. 基于石墨烯基底的光催化特性 [J]. 光谱学与光谱分析, 2022, 42(04): 1058-1063.
[5]
. 丝网印刷制备染料敏化太阳能电池 [J]. 光谱学与光谱分析, 2021, 41(07): 2321-2324.
[6]
. 泡沫镍网负载Ag3 PO4 /GO的光谱特性及光催化降解乙烯性能研究 [J]. 光谱学与光谱分析, 2020, 40(09): 2743-2750.
[7]
. 改性丙烯酸水性漆对漆膜性能的影响 [J]. 光谱学与光谱分析, 2020, 40(07): 2133-2137.
[8]
. 硝酸辅助合成氮缺陷石墨型氮化碳材料及光谱学分析 [J]. 光谱学与光谱分析, 2020, 40(07): 2159-2163.
[9]
. 基于紫外LED阵列光催化降解抗生素的研究 [J]. 光谱学与光谱分析, 2019, 39(09): 2894-2900.
[10]
. FTIR与XRD的均匀粒度分布Ce-Cu/TiO2 空心微球制备机理研究 [J]. 光谱学与光谱分析, 2019, 39(08): 2360-2365.
[11]
. BiOCl1-x Ix 及BiOBr1-x Ix 固体溶液的制备、表征及性能研究 [J]. 光谱学与光谱分析, 2019, 39(08): 2443-2449.
[12]
. 离子液体在大气压等离子体中稳定性研究 [J]. 光谱学与光谱分析, 2019, 39(05): 1372-1376.
[13]
. DBU液相催化法原位合成四苯氧基酞菁锌/ZnO复合材料的制备及光催化选择性研究 [J]. 光谱学与光谱分析, 2018, 38(05): 1486-1491.
[14]
. 石墨烯改性锡酸锌材料的光谱特性及其光催化性能 [J]. 光谱学与光谱分析, 2018, 38(04): 1219-1224.
[15]
. SO2- 4 /CeO2 -TiO2 光催化材料的制备与光谱表征 [J]. 光谱学与光谱分析, 2017, 37(10): 3315-3320.