Effect of Heating and Cooling on the Characteristic Lines of Al During Melting
GONG Zheng1, LIN Jing-jun2*, LIN Xiao-mei3*, HUANG Yu-tao1
1. Department of Electronics and Electrical Engineering, Changchun University of Technology, Changchun 130012, China
2. Department of Mechanical and Electrical Engineering, Changchun University of Technology, Changchun 130012, China
3. Jilin University of Architecture and Technology，Changchun 130114, China
Abstract：In order to solve the problem of low accuracy and poor repeatability caused by temperature change when LIBS technology is applied to the analysis of metallurgical process composition, the influence of temperature change on plasma is studied in this paper. The results show that the intensity of the characteristic lines of Al increases with the increase of temperature and reaches saturation at 700 ℃. When the temperature rises to 700, 500 and 200 ℃, Al I increases When the sample temperature is 700 ℃, the plasma electron temperature rises to 13122 K, and the electron density increases to 4.65×1016 cm-3 respectively. In the first stage, the sample stops heating and naturally cools down, and the plasma parameters drop rapidly with the sample temperature; in the second stage, when the sample temperature drops to about 660 ℃, the spectral intensity decreases slowly and becomes stable. At this time, the plasma electron The temperature was stable at about 16 000 K, and the electron density was 7.6×1016 cm-3; in the third stage, the plasma characteristic parameters continued to decrease until the sample temperature dropped to room temperature. When LIBS technology is applied to the detection of molten metal components, the best measurement point can be obtained by controlling the sample temperature, there by improving the detection accuracy of LIBS technology.
Key words：Laser induced breakdown spectroscopy; Sample temperature; Electron temperature; Electron density
公 正，林京君，林晓梅，黄玉涛. 熔融过程中升温和降温对Al特征谱线的影响[J]. 光谱学与光谱分析, 2022, 42(02): 598-602.
GONG Zheng, LIN Jing-jun, LIN Xiao-mei, HUANG Yu-tao. Effect of Heating and Cooling on the Characteristic Lines of Al During Melting. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(02): 598-602.
[1] Guo L B, Zhu Z H, Li J M, et al. Optics Express, 2018, 26(3): 2634.
[2] Zhang G Y, Song H, Liu Y, et al. Optik, 2018, 165(5): 87.
[3] YANG You-sheng, ZHANG Yan, YANG You-liang, et al(杨友盛, 张 岩, 杨友良, 等). Laser & Optoelectronics Progress(激光与光电子学进展), 2015, 52(5): 209.
[4] Sturm V, Fleige R, De K M, et al. Analytical Chemistry, 2014, 86(19): 9687.
[5] Lednev V N, Grishin M Y, Sdvizhenskii P A, et al. Journal of Analytical Atomic Spectrometry, 2019, 34(3)：607.
[6] Gill R K, Smith Z J, Lee C, et al. Journal of Biophotonics, 2016, 9(1-2): 171.
[7] Li T, Hou Z, Fu Y, et al. Analytica Chimica Acta, 2019，1058：39.
[8] Mansour S A M. Optics & Photonics Journal, 2015, 5(3): 79.
[9] WANG Li, FU Yuan-xia, XU Li(王 莉，傅院霞，徐 丽). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2019, 39(4): 1248.
[10] Shao J F, Guo J, Wang Q, et al. Plasma Science and Technology, 2020, 22(7)：8.
[11] Cui M C, Deguchi Y, Wang Z, et al. Plasma Science and Technology, 2019, 21(3)：56.
[12] Liu Y, Tong Y, Li S, et al. Chinese Optics Letters, 2016，14(12)：136.
[13] Liu Y, Tong Y, Wang Y. Plasma Science and Technology, 2017, 19(12): 125501.
[14] Wang Y, Chen A, Jiang Y, et al. Physics of Plasmas, 2017, 24(1): 013301.
[15] Guo Y M, Deng L M, Yang X Y, et al. Journal of Analytical Atomic Spectrometry, 2017, 32(12): 2401.