Abstract:The contents of holocellulose and lignin of wood are important determinants of the pulping quality of wood. The determination of holocellulose and lignin contents using traditional chemical methods is a costly and time-consuming process. Near infrared reflectance (NIR) analysis offers a fast,nondestructive testing and low cost alternative for prediction of wood quality. In the present article,the total amounts of holocellulose and lignin contents of 48 samples were analyzed according to standard wet-chemical method. All samples were milled using a Standard Wiley knife mill with a 2 mm screen. The 2 mm material was sieved with a 40-60 mesh sieve. Then,near infrared (NIR) spectra were collected in diffuse reflectance from samples of meal contained in a spinning cup by an analytical spectral devices (ASD) Lab Spec at wavelengths between 350 nm and 2 500 nm. The raw spectra were pretreated by the second derivative and smoothing,then the NIR model was built using partial least-squares statistical analysis and full cross validation. The coefficients of correlation (r) of calibration and validation for holocellulose were 0.96 and 0.93,respectively;the standard error of calibration (SEC) and the standard error of prediction (SEP) were 0.39 and 0.50,respectively. For lignin,the values for r of calibration and validation were 0.99 and 0.90,while the SEC and SEP were 0.10 and 0.28,respectively. It was concluded that NIR analysis is a reliable,fast and nondestructive testing predictor of holocellulose and lignin content of wood in Chinese fir.
黄安民,江泽慧*,李改云. 杉木综纤维素和木质素的近红外光谱法测定[J]. 光谱学与光谱分析, 2007, 27(07): 1328-1331.
HUANG An-min,JIANG Ze-hui*,LI Gai-yun. Determination of Holocellulose and Lignin Content in Chinese Fir by Near Infrared Spectroscopy. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(07): 1328-1331.
[1] ZHANG Lu-da,WANG Tao,YANG Li-ming,et al(张录达,王 韬,杨丽明,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2005,25(12): 1959. [2] LU Wan-zhen,YUAN Hong-fu,XU Guang-tong,et al(陆婉珍,袁洪福,徐广通,等). Modern Near Infrared Spectroscopy Analysis Technology(现代近红外分析技术). Beijing: China Petrochemical Press(北京: 中国石化出版社),2001. [3] JIANG Ze-hui,HUANG An-min,FEI Ben-hua,et al(江泽慧,黄安民,费本华,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2006,26(7): 1230. [4] YANG Shu-hui(杨淑蕙). Lignocellulosic Fiber Chemistry(植物纤维化学). Beijing: China Light Industry Press(北京: 中国轻工业出版社),2001. [5] Sake S. Cellulose Chemistry and Technology,1987,21(3): 225. [6] Schimleck L R,Michell A J,Raymond C A,et al. Journal of Near Infrared Spectroscopy,1998,6: 117. [7] Schimleck L R,Michell A J,Raymond C A,et al. Canadian Journal of Forest Research,1999,29(2): 194. [8] Schimleck L R,Evans R. IAWA Journal,2002,23(3): 225. [9] Schimleck L R,Evans R,Ilic J. Canadian Journal of Forest Research,2001,31(10): 1671. [10] Kelley S S,Rials T G,Snell R,et al. Wood Science and Technology,2004,38(4): 257. [11] Hodge G R,Woodbridge W C. Journal of Near Infrared Spectroscopy,2004,12(6): 381. [12] Martin M E,Aber J D. Journal of Near Infrared Spectroscopy,1994,2(1): 25. [13] Yamada T,YEH Ting-feng,CHANG Hou-min,et al. Holzforschung,2006,60(1): 24. [14] Wright J A,Birkett M D,Gambino M J T. TAPPI Journal,1990,73(8): 164. [15] Hoffmeyer P,Pedersen J G. Holz als Roh-und Werkstoff,1995,53: 165. [16] JIANG Ze-hui,HUANG An-min,WAN Bin(江泽慧,黄安民,王 斌). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2006,26(6): 1034. [17] JIANG Ze-hui,HUANG An-min(江泽慧,黄安民). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2006,26(8): 1464. [18] JIANG Ze-hui,FEI Ben-hua,YANG Zhong(江泽慧,费本华,杨 忠). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2007,27(3): 435. [19] YANG Zhong,JIANG Ze-hui,FEI Ben-hua(杨 忠,江泽慧,费本华). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2007,27(4): 686. [20] JIANG Ze-hui,LI Gai-yun,WANG Ge(江泽慧,李改云,王 戈). Chemistry & Industry of Forest Products(林产化学与工业),2007,27(1): 15.