The Silver Surface Plasmon Enhancement for Er3+ Ion Upconversion of 978 and 1 539 nm Laser in Bismuth Glass
CHEN Xiao-bo1, LI Song1, ZHAO Guo-ying2, LONG Jiang-mi1, WANG Shui-feng1, MENG Shao-hua2, WANG Jie-liang1, GUO Jing-hua1, YOU Jia-jia1, MA Yu2, YU Chun-lei3, HU Li-li3
1. Applied Optics Beijing Area Major Laboratory, Beijing Normal University, Beijing 100875, China
2. School of Materials Science and Technology, Shanghai Institute of Technology, Shanghai 200235, China
3. Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China
Abstract:Upconversion luminescence of trivalent rare-earth ions has some valuable application technologies: Waveguide upconversion and amplification and laser, Up-conversion three-dimensional display, Femtosecond spectral applications, Laser temperature control, Three-dimensional imaging and storage, Optical temperature sensing system, Dental and other biophysical applications, Up-conversion fluorescence anti-counterfeiting, Up-conversion broadband light source, and Up-conversion infrared display, etc.Promoted by the demand for solar cells, up-conversion research has once again shown a surging upsurge of research. Current, using the near field enhancement effect of metal surface Plasmon resonance can effectively enhance the luminescent properties of fluorescent substances near its surface. It is possible to increase the intensity of upconversion luminescence by a considerable margin. Thus, it is possible to promote up-conversion luminescence to practical use further. We use the ion introduction method to introduce silver particles into bismuth luminescent glass. Experimental results show that the surface Plasmon resonance absorption peak of silver surface Plasmon is positioned at about 580~600 nm. Moreover, the prolongation of heating time leads to a sharp enhancement and a slight blue shift of the surface Plasmon absorption peak. Subsequently, we find that three groups two-photon upconversion fluorescence of 531.0 nm 2H11/2→4I15/2, 546.0 nm 4S3/2→4I15/2, and 657.5 nm 4F9/2→4I15/2of Er3+ ions can be induced by the 978 nm laser. Upconversion luminescence mechanism, when erbium doped bismuth luminescent glass excited by 978 nm laser, is the first step 4I15/2→4I11/2resonance ground state absorption and the second step 4I11/2→4F7/2 resonance excited state absorption. The introduction of silver nano surface Plasmon facilitates that the maximum enhancement of upconversion luminescence is 272.0% times bigger in bismuth glass, when excited by 978 nm laser. Finally, the 1 539 nm laser can induce four groups upconversion fluorescence of 528.0 nm 2H11/2→4I15/2, 547.0 nm 4S3/2→4I15/2, 657.0 nm 4F9/2→4I15/2, and 795.0 nm 4I9/2→4I15/2 of Er3+ ion. The mechanism of 528.0 nm 2H11/2→4I15/2 and 547.0 nm 4S3/2→4I15/2 upconversion luminescence is mainly 4I15/2→4I13/2, 4I13/2→4I9/2, and 4I9/2→2H11/2three-step photo-excited absorption transition process of 1539 nm laser. The mechanism of 657.0 nm 4F9/2→4I15/2 upconversion fluorescence is mainly the 4I15/2→4I13/2, 4I13/2→4I9/2, and 4I11/2→4F9/2 three-step photo-excited absorption transition process of 1 539 nm laser. Furthermore, the introduction of silver nano surface Plasmon induces that the maximum enhancement of up-conversion luminescenceof Er3+ ionstimulated by 1 539 nm laser is 160.3% times bigger in bismuth glass. Obviously, the enhancement effect of 978 nm laser upconversion, which is near the resonance absorption peak of silver surface Plasmon, is better than that of 1 539 nm laser upconversion.
陈晓波,李 崧,赵国营,龙江迷,王水峰,孟少华,王杰亮,郭敬华,尤佳佳,马 瑜,于春雷,胡丽丽. 银表面等离子体对掺铒铋化物发光玻璃中978和1 539 nm激光所致上转换发光的增强作用[J]. 光谱学与光谱分析, 2020, 40(09): 2721-2726.
CHEN Xiao-bo, LI Song, ZHAO Guo-ying, LONG Jiang-mi, WANG Shui-feng, MENG Shao-hua, WANG Jie-liang, GUO Jing-hua, YOU Jia-jia, MA Yu, YU Chun-lei, HU Li-li. The Silver Surface Plasmon Enhancement for Er3+ Ion Upconversion of 978 and 1 539 nm Laser in Bismuth Glass. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2721-2726.
[1] Wang Q R, Zhang J, Sang X, et al. Journal of Luminescence, 2018, 204: 284.
[2] Wang C, Zhu W, Li G T, et al. Journal of Physical Chemistry C, 2014, 118(20): 10754.
[3] Yin Z, Xu W, Song H W, et al. Advanced Materials, 2016, 28(13): 2518.
[4] Zhan Q Q, Zhang X, He S L, et al. Laser & Photonics Reviews, 2015, 9(5): 479.
[5] Luo Q, Chen Y R, Li Z Q, et al. Nanotechnology, 2014, 25(18): 185401.
[6] Dong J, Zhang Z L, Sun M T, et al. Nanophotonics, 2015, 4(4): 472.
[7] Kuai Y, Chen J X, Lakowicz J R, et al. Science Advances, 2019, 5(3): eaav5335.
[8] Zhao G Y, Xu L Z, Meng S H, et al. Journal of Luminescence, 2019, 206: 164.
[9] LIU Shao-ding(刘绍鼎). Surface Plasmon Resonance and Its Application in Metal-Nanometer System(金属钠米体系表面等离激元共振及应用). Beijing: National Defense Industry Press(北京:国防工业出版社), 2013.
[10] Kassab L R P, Kumada D K, da Silva D M, et al. Journal of Non-Crystalline Solids, 2018, 498: 395.
[11] Jia X M, Xia M L, Dai S X, et al. Optical Materials Express, 2018, 8(6): 1625.
[12] Fang Y Z, Zhao G Y, Hu L L, et al. Journal of Alloys and Compounds, 2019, 809: UNSP 151725.