Abstract：Stable pseudo-boehmite sol was obtained by adding HNO3 as peptizing agent and adjusting pH to be 2.0. TEM result shows that the AlOOH colloidal particle size is about 60 nm. Field emission transmission electron microscope (FETEM) result shows that pseudo-boehmite colloidal particle is composed of 8nm scaled AlOOH nanocrystals. The interaction of Eu3+ ions and colloidal AlOOH nanoparticle was investigated. The adsorption of Eu3+ ions on the surface of AlOOH nanocrystal was attributed to the chemical adsorption caused by electrostatic attraction. The photoluminescence characters of Eu3+ in AlOOH/Eu(NO3)3 composite sol system were investigated. The 529 nm emission intensity of Eu3+,I592,decreased with the increase in the molar ratio of AlOOH and Eu3+,RBoe/Re. The adsorption ratio (denoted R) and the adsorption density (denoted D) of Eu3+ ions on AlOOH colloidal particle surface was calculated from I592. The results show that the values of R and D increase with increasing RBoe/Re.
[1] Cvjeticanin D, Cvjeticanin N, Pravica M. Journal of Chromatography A, 1984, 286(23): 139. [2] Koeppenkastrop D, Crio E H D. Environ Sci. Tec., 1993, 27: 1796. [3] Hiemstra T, Vanriemsdijk W H, Bolt G H. Journal of Colloid and Interface Sci., 1989, 133(1): 91. [4] QUAN Guang-ri, PU Xu-li, JIANG Zu-cheng(全光日，普旭力，江祖成). Chinese Journal of Analytical Chemistry(分析化学)，2005，33(2)：207. [5] WANG Da-jian(王达健)，Patent(中国专利)，CN03117872.3，2003. [6] ZHONG Ming-hua, QIU Xue-ting, MO Chun-sheng, et al(衷明华，邱学婷，莫春生，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，1999，19(1)：84. [7] FAN Zhe-feng, DU Li-ming, JIN Xiao-tao(范哲锋，杜黎明，靳晓涛). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2003, 23(2): 365. [8] WANG Jian-qiang, GUO Ping-jun, QIAO Ming-hua(王建强，郭平均，乔明华). Chinese Journal of Chemistry(化学学报)，2004，62(18): 1765. [9] HU Ping, ZHAO Ling-hu, YIN Xiu-lan(胡 萍，赵令湖，殷秀兰). Acta Mineralogica Sinica(矿物学报), 2005, 25(3): 263.